How to make the color of vacuum titanium
In the product, before the titanium plating, if the product itself is covered with oxide (or sand and pour), then the point of titanium oxide (or sand and pore) after titanium plating is called the weak point. The substrate itself is not strong enough. After a period of time, the substrate layer of titanium oxide on the point of that is easy to fall off, so rust and titanium of phenomenon. General sanding product polishing time, resulting in a large friction coefficient, the product surface is exposed to oxide. The reason why the plated titanium knife will produce rust, titanium plating process is due to the vacuum conditions, the product of the sand and pores of the substrate impurities are cleaned up, the product surface sand holes and stomata formed concave, The titanium can not be completely filled after the sand hole and pores, the use of the tool, the residual sand and pores in the water has not been cleaned up, so sand holes and stomata easily oxidized to produce rust.
How to place a solid titanium film?
Vacuum titanium is the vacuum environment, the use of arc discharge, the cathode titanium target as the evaporation source through the titanium target and the anode arc discharge between the body, the titanium target evaporation and the formation of ions, resulting in high-speed ion body To the product movement, the product surface deposition, the formation of a titanium coating. In high vacuum and high temperature titanium environment, different games can be played with different colors. Such as adding N2, plated out the color is golden; and C2H2, the color is black; add O2, the color will be coloured and blue; such as adding N2 and C2H2, the color will be rose gold. In the process of titanium plating, the materials used are titanium and high-purity gas, all of which are green materials. Since they are produced by a high-temperature vacuum environment and do not produce any harmful substances, plated products are very safe and environment- can pass a variety of safety tests.
To build a solid layer of titanium, first of all has good equipment. Because the coating process, the vacuum system must be stable, the furnace pressure is better, if there is mixed with impurities in the coating process, the color will be unsatisfactory, but also serious titanium. Good equipment arc source ionization rate is high, the formation of ion density, large particles less plated plated layer of high smoothness, small friction coefficient, solid does not fall off, poor equipment, low rate of ionization, plating out of the film Rough dull, easy to scratch off.
In the product, before the titanium plating, if the product itself is covered with oxide (or sand and pour), then the point of titanium oxide (or sand and pore) after titanium plating is called the weak point. The substrate itself is not strong enough. After a period of time, the substrate layer of titanium oxide on the point of that is easy to fall off, so rust and titanium of phenomenon. General sanding product polishing time, resulting in a large friction coefficient, the product surface is exposed to oxide. The reason why the plated titanium knife will produce rust, titanium plating process is due to the vacuum conditions, the product of the sand and pores of the substrate impurities are cleaned up, the product surface sand holes and stomata formed concave, The titanium can not be completely filled after the sand hole and pores, the use of the tool, the residual sand and pores in the water has not been cleaned up, so sand holes and stomata easily oxidized to produce rust.
How to place a solid titanium film?
Vacuum titanium is the vacuum environment, the use of arc discharge, the cathode titanium target as the evaporation source through the titanium target and the anode arc discharge between the body, the titanium target evaporation and the formation of ions, resulting in high-speed ion body To the product movement, the product surface deposition, the formation of a titanium coating. In high vacuum and high temperature titanium environment, different games can be played with different colors. Such as adding N2, plated out the color is golden; and C2H2, the color is black; add O2, the color will be coloured and blue; such as adding N2 and C2H2, the color will be rose gold. In the process of titanium plating, the materials used are titanium and high-purity gas, all of which are green materials. Since they are produced by a high-temperature vacuum environment and do not produce any harmful substances, plated products are very safe and environment- can pass a variety of safety tests.
To build a solid layer of titanium, first of all has good equipment. Because the coating process, the vacuum system must be stable, the furnace pressure is better, if there is mixed with impurities in the coating process, the color will be unsatisfactory, but also serious titanium. Good equipment arc source ionization rate is high, the formation of ion density, large particles less plated plated layer of high smoothness, small friction coefficient, solid does not fall off, poor equipment, low rate of ionization, plating out of the film Rough dull, easy to scratch off.