| Product name | grade 2 titanium sheet |
| Standard |
ASTM B265,ASME SB265,AMS 4911,ASTM F67,ASTM F136 ISO5832-2,ISO5832-3 |
| Thickness | 0.3-60mm |
| Width | ≤3,000mm |
| Length | ≤12,000mm |
| Grade | Gr1, Gr2, Gr5, Gr7, Gr9, Gr10, Gr12, Gr23, etc. |
| Special |
T(4.0-60.0) × W(100-3000) × L(1000-12000)mm T(0.3- 4.0) × W(100-1000) × L(1000-12000)mm |
| Features |
1.high corrosion resistance 2.low density 3.non-ferromagnetic 4.good biocompatibility |
| The specification can be changed by the customers' requirements. | |
grade 2 titanium sheet
grade 2 titanium sheets American Standard: ASTM B265, ASTM F136, ASTM F67, AMS4928
grade 2 titanium sheet production specifications
T 0.5-1.0mm x W1000mm x L 2000-4000mm
T 1.0-5.0 mm x W1000-1500 mm x L 2000-3500 mm
T 5.0 - 30mm x W1000-2500mm x L 3000-6000mm
T 30- 80mm x W1000mm x L 2000mm
grade 2 titanium sheet manufacturing process hot forging: grade 2 titanium sheet in the metal recrystallization temperature above the forging process.
grade 2 titanium sheet Hot Rolling: Rolling process at higher than recrystallization temperature. grade 2 titanium sheet cold rolling: plastic deformation temperature is lower than the recovery temperature of the rolling process.
grade 2 titanium sheet Annealing: A metal heat treatment process in which the metal is slowly heated to a certain temperature, maintained for a sufficient time, and then cooled at a suitable speed (usually slow cooling, sometimes controlled cooling).
Pickling: The part is immersed in an aqueous solution of sulfuric acid or the like to remove a thin film such as an oxide on the metal surface. Is electroplating, enamel, rolling and other pre-treatment or intermediate processing